This product is made from high-quality raw materials using a unique molding technique. The ceramic board features interconnected channels inside, giving it excellent capillary carbon (C) storage performance. With uniform pore size and high porosity (30%-50%), it significantly enhances breathability. This series of porous ceramic plates offers excellent permeability, high-temperature resistance, corrosion resistance, superior insulation, lightweight design, and low thermal mass. Its extremely smooth surface prevents scratches during the shrinkage of metal pastes, making it ideal for use as sintering support plates and leveling press plates in HTCC, LTCC, titanium alloy, and other products.

Product Technical Parameters

Item	Technical parameters	Technical parameters	Technical parameters
Material	Alumina	Alumina-containing zirconia	Calcia-stabilized zirconia
Composition	AL2O3:≥99.5%	ZrO2+AL2O3≥99.9%	ZrO2+CaO≥99.9%
Porosity	30-50%	30-50%	30-50%
Channel diameter	0.5-1μm	0.5-1μm	0.5-1μm
Compressive strength	≈20Mpa	≈20Mpa	≈20Mpa
Thickness	1.5-5mm customized
Maximum width	≤210mm
Maximum length	≤400mm
‌Recommended use	LTCC, HTCC, titanium alloy, hydrogen fuel cell, oxygen sensor

None

Corundum Mullite Sintering Plate

Contact Now

Address: No.1 Chongwen Road, Yancheng Coastal Cooperative Development Park, Dafeng District, Yancheng City, Suzhou

Mr. Li: +86 18051260171

Email: liming@ruibanggs.com

Mr. Wei: +86 15850077898

Email: wgw@ruibanggs.com

Send email

My business card
Ruibang products

Official website

Business License